GHID CORESPONDENTA OTELURI

GHIDPRIVIND CORESPONDENTA MATERIALELOR(valabil pentru mentenanta mijloacelor)F115.20-04-002RA, vers 01Uz intern : AUTOMOBILE DACIAData elaborarii: martie 2004Elaborat : Vasile BAIASUCUPRINS 1. OTELURI LAMINATE SI TRASE1.1. OTEL DE UZ GENERAL PENTRU CONSTRUCTII1.2. OTEL CARBON DE CALITATE PENTRU TRATAMENT TERMIC, DESTINAT CONSTRUCTIEI DE MASINI1.3. OTEL PENTRU ARCURI1.4. OTEL ALIAT PENTRU TRATAMENT TERMIC IN CONSTRUCTIA DE MASINI1.5. OTEL RAPID PENTRU SCULE1.6. OTEL PENTRU SCULE1.7. OTEL ALIAT PENTRU SCULE1.8. OTEL REZISTENT LA COROZIUNE SI 14414p1519o REFRACTAR, PRELUCRAT LA CALD1.9. OTEL INOXIDABIL SI REFRACTAR1.10. OTEL PENTRU RULMENTI1.11. OTEL REZISTENT LA UZURA1.12. OTEL PENTRU AUTOTURISME DACIA1.13. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA RIDICATA1.14. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA SI SCAZUTA1.15. OTEL PENTRU AUTOTURISME DACIA1.16. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI RIDICATE1.17. OTEL CU GRANULATIE FINA PENTRU TABLE DESTINATE CONSTRUCTIILOR SUDATE1.18. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI SCAZUTE1.19. OTEL PENTRU TABLE SI BENZI DESTINATE AMBUTISARII1.20. OTEL PENTRU TABLE SI BENZI LAMINATE LA RECE DESTINATE CAROSERIILOR AUTO1.21. OTEL REZISTENT LA COROZIUNE1.22. OTEL PENTRU AUTOMATE1.23. OTEL PENTRU PINIOANE1.24. OTEL PENTRU ORGANE DE ASAMBLARE1.25. OTEL PENTRU TEVI FARA SUDURA, DE UZ GENERAL1.26. OTEL PENTRU SUPAPELE MOTOARELOR CU ARDERE INTERNA1.27. OTEL PENTRU SUPAPE EVACUARE1.28. OTEL TERMOREZISTENT PENTRU ORGANE DE SAMBLARE2. OTELURI TURNATE 2.1. OTEL SLAB ALIAT SI ALIAT TURNAT IN PIESE2.2. OTEL AUSTENITIC MANGANOS TURNAT IN PIESE2.3. OTEL TURNAT IN PIESE PENTRU ARMATURI2.4. OTEL CARBON, SLAB ALIAT REZISTENT LA TEMPERATURI RIDICATE, TURNAT IN PIESE 3. FONTE3.1. FONTE CU GRAFIT LAMELAR3.2. FONTE CU GRAFIT NODULAR3.3. FONTE MALEABILE3.4. FONTE CU GRAFIT NODULAR CU STRUCTURA BAINITICA

1. oteluriRecomandari de utilizare:· Corespondenta marcilor de oteluri laminate sau trase este in conformitate cu STAS R 4400/1-80.

· Corespondenta indicata este aproximativa si data cu titlu informativ. Ea este stabilita pe baza : compozitiei chimice, caracteristicilor mecanice si a conditiilor de utilizare.· Pentru marcile straine indicate intre paranteze corespondenta stabilita este foarte larga.1.1. OTEL DE UZ GENERAL PENTRU CONSTRUCTII

STAS 500/2-80 NFA 35-501-77

DIN 17100Marca Numar

OL 34.1 A 34-1 USt 34-1 1.0055OL 37.1OL 37.2OL 37.2kOL 37.3OL 37.4

E 24-1E 24-2 (S235JR)E 24-2NEE 24-3E 24-4

USt 37-1USt 37-2RSt 37-2St 37-3St 37-3

1.00651.00361.00381.01161.0116

OL 42.1OL 42.1kOL 42.2OL 42.2kOL 42.3-

E 26-1E 26-1NEE 26-2E 26-2NEE 26-3E 26-4

USt 42-1RSt 42-1USt 42-2RSt 42-2St 42-3St 42-3

1.00751.00771.00401.00421.01361.0136

OL 44.2(k)OL 44.3(k)OL 44.4(k)

E 30-2E 30-3E 30-4

RSt 46-2St 46-3St 46-3

1.04771.04831.0483

OL 52.2(k)OL 52.3(k)OL 52.4(k)

E 36-2E 36-3E 36-4

-St 52-3St 52-3

-1.05701.0570

OL 50(k) A 50-2 St 50-2 1.0050OL 60(k) A 60-2 St 60-2 1.0060OL 70(k) A 70-2 St 70-2 1.0070OL 30 A 33-1

A 33-2 St 33-1St 33-2

1.00331.0035

1.2. OTEL CARBON DE CALITATE PENTRU TRATAMENT TERMIC, DESTINAT CONSTRUCTIEI DE MASINISTAS 880-80 NF

A 35-551-72A 35-552-72

DIN17200-6917210-69Marca Numar

OLC 10OLC 10 X

CC 10 , (AF 34 C 10)*XC 10

C 10Ck 10

1.03011.1121

OLC 15OLC 15 X

AF 37 C 12)*XC 18, (XC 15)

C 15Ck 15

1.04011.1141

OLC 20 CC 20 - -OLC 25OLC 25 X

(AF 42 C 20)*XC 25, (XC 18)

C22Ck 22

1.04021.1151

OLC 35OLC 35 X

CC 35, (AF 55 C 35)*XC 38, (XC 35), (XC 32)

C 35Ck 35

1.05011.1181

OLC 45OLC 45 X

CC 45,(AF 65 C 45)*XC 48, (XC 45), (XC 42)

C 45Ck 45

1.05031.1191

OLC 55OLC 55 X

XC 55, (XC 54) C 55Ck 55

1.05351.1203

OLC 60OLC 60X

(AF 70 C 55)*XC 60, (XC 65)

C 60Ck 60

1.06011.1221

*simbolizare veche1.3. OTEL PENTRU ARCURI

STAS 795-80 NFA 35-551-72A 35-552-72A 35-571-74


OLC 55 A XC 55 Ck 55 1.1203OLC 65 A(OLC 66 SSTAS 8371-80)

XC 68 (XC 65) Ck 67 1.1231

OLC 75 A XC 75 Ck 75 1.1248OLC 85 A - Ck 85 1.126951 Si 17 A 51 S 7 51 Si 7 1.090340 Si 17 A (45 S 7) - -51 VCr 11 A 50 CV 4 50CrV 4 1.815956 Si 17 A 55 S 7 55 Si 7 1.090460 Si 15 A - 60SiCr7 1.710865 S 2 WA(STAS 11514-80)

- - -

1.4. OTEL ALIAT PENTRU TRATAMENT TERMIC IN CONSTRUCTIA DE MASINISTAS 791-80 NF

A 35-551-72A 35-552-72A 35-571-74


15 Cr 08 - (15 Cr 3) 1.701518 MnCr 10 16 MC 5 16 MnCr 5 1.713121 MoMnCr 12 (18 CD 4) - -18 MoCrNi 13 18 NCD 6

18 CND 617 CrNiMo 6 1.6587

13 CrNi 30 (14 NC 11)(16 NC 11)

(14 NiCr 10) 1.5732

20 MoNi 35 - - -21 TiMnCr 12 - - -28 TiMnCr 12 - - -35 Mn 16 - - -65 Mn 10 - 65 Mn 4 1.281735 MnSi 12 - 37 MnSi 5 1.512240 Cr 10 42 C 4 41 Cr 4 1.703540 BCr 10 - - -33 MoCr 11 34 CD 4

(35 CD 4)34 CrMo 4 1.7220

41 MoCr 11 (38 CD 4)40 CD 442 CD 4

42 CrMo 4 1.7225

50 VCr 11 50 CV 4 50 CrV 4 1.815934 MoCrNi 15 (35 NCD 6) 34 CrNiMo 8 1.6582

30 MoCrNi 20 30 CND 830 NCD 8

30 CrNiMo 8 1.6580

38 MoCrAl 09 (40 CAD 6.12) (34 CrAlMo 5)(41 CrAlMo 7)

1.85071.8509

41 CrNi 12 (30 NC 12) (31 NiCr 14) 1.575218 CrNi 20 20 NC 6 18 CrNi 8 1.5920

1.5. OTEL RAPID DE SCULESTAS 7382-80 NF

A 35-590-78SEW320-69Marca Numar

Rp 1 - - -Rp 2 Z 80 WKCV 18.05.04.01 HS 18-1-2-5 1.3255Rp 3 (Z80 WCV 18.04.01) HS 18-0-1 1.3355Rp 5 Z 85 WDCV 06.05.04.02 HS 6-5-2C 1.3343Rp 9 - HS 3-3-2 1.3333Rp 10 Z 85 DCWV 08.04.02.02 HS 2-9-1 1.3346- Z 110 WKDV 07.05.04.02 HS 7-4-2-5- Z 120 WDV 06 HS 6-5-3- Z 150 WKV 12 HS 12-4-5-5- Z 110 DKWV 09.08.02.01 HS 2-9-1-8- Z 160 WDV 06 HS 6-5-3- Z 110 DK 09 (lame de forma, scule

GLEASON) 1.6. OTEL PENTRU SCULE

STAS 1700-80 NFA 35-590-78

SEW150-71Marca Numar

OSC 7 Y1 70 (C 67 W3) 1.1744OSC 8 Y1 80

Y1 90C 80 W 1C 80 W 2

1.15251.1625

OSC 10 Y1 105 (C 105 W 1)(C 105 W 2)

1.15451.1645

OSC 11 - C 110 W 2 1.1654OSC 13 -

--

(C 125 W 1)(C 125 W 2)(C 135 W 2)

1.15601.16631.1673

1.7. OTEL ALIAT PENTRU SCULESTAS 3611-80 NF

A 35-590-78SEW 200-69SEW 250-70Marca Numar

MCV 14 105 WC 13 105 WCr 6 1.2419VM 18 90 MV 8 90 MnCrV 8 1.2842CW 20 (105 WC 13) (105 WCr 6) 1.2419C 120 Z 200 C 12 X 210 Cr 12 1.2080VMoC 120 Z 160 CDV 12 X 153 CrMoV 12 1.2601CV 06 - 115 CrV 3 1.2210VCW 85 Z 30 WCV 9 X 30 WCrV9 3 1.2581MoCN 15 - 55 NiCrMoV 6 1.2713VMoCN 17 55 NCDV 7 56 NiCrMoV 7 1.2714MoVC 30 32 DCV 5 X 32 CrMoV 3 3 1.2365- 35 CDV 5 X 100 CrMoV 5MoVC 50.10 Z 38 CDV 5 X 37 CrMoV 5 1 1.2343MoVC 50.13 Z 40 CDV 5 X 40 Cr MoV 5 1 1.2344

MoWC 53 - X 37 CrMoW 5 1 1.2606VSCW 20 - 45 WCrV 7 1.2542

1.8. OTEL REZISTENT LA COROZIUNE SI REFRACTAR, PRELUCRAT LA CALDSTAS 3583-80 NF

A 35-572-75A 35-578-70

DIN 17440-72SEW 470-76Marca Numar

12 Cr 130 Z 12 C 13 X 10 Cr 13 1.400620 Cr 130 Z 20 C 13 X 20 Cr 13 1.402130 Cr 130 Z 30 C 13 X 30 Cr 13 1.402840 Cr 130 - X 40 Cr 13 1.40348 (Ti)Cr 170 Z 8 C 17 X 8 Cr 17

X 6 Cr Ti 171.40161.4510

12 NiCr 180 (Z 10 CN 18.09) X 12 CrNi 18 8 1.430010 TiNiCr 180(STAS 10322-80)

Z 6 CNT 18.10 X 10 CrNiTi 18 9 1.4541

10 TiMoNiCr 175 Z 6 CNDT 17.12 X 10 CrNiMoTi 18 10 1.457115 SiNiCr 250(Cr 25 Ni 20 STAS 11510-80)

Z 12 CNS 25.20 X 15 CrNiSi 25 20 1.4841

1.9. OTEL INOXIDABIL SI REFRACTARSTAS 11523-80 NF

A 35-572-75A 35-576-75A 35-578-70A 35-583-75

DIN 1770-72SEW 400-73SEW 470-76SEW 670-69Marca Numar

7 AlCr 130 Z 6 CA 13 X 7 CrAl 13 1.400222 NiCr 170 Z 15 CN 16.02 X 22 CrNi 17 1.405790 VmoCr 180 Z 100 CD 17 X 90 CrMoV 18 1.411235 MoCr 165 - X 35 CrMo 17 1.41222 NiCr 185 Z 2 CN 18.09

Z 2 CN 18.10X 2 CrNi 18 9 1.4306

2 MoNiCr 175 Z 2 CND 17.12 X 2 CrNiMo 18 12 1.44352 CuMoCrNi 250 Z 1 NCDU 25.20 (X 2 NiCrMoCu 25 21) 1.453610 AlCr 240 Z 10 CAS 24 X 10 CrAl 24 1.476215 SiNiCr 200 Z 15 CNS 20.15 X 15 CrNiSi 20 12 1.482812 NiCr 250 Z 12 CN 25.20 X 12 CrNi 25 21 1.48452 NiCr 250 Z 2 CNNb 25.20 (X 5 CrNi 25 21) 1.433512 SiCrNi 360 Z 12 NCS 35.16 X 12 NiCrSi 36 16 1.486440 SiCrNi 380 - X 40 NiCrSi 36 16 1.486510 TiAlCrNi 320 - X 10 NiCrAlTi 32 20 1.487612 TiNiCr 180 Z 6 CNT 18.12 B X 12 CrNiTi 18 9 1.487819 MoCr 120 - X 19 CrNiTi 12 1 1.492120 VWMoCr 120 - X 20 CrMoWV 12 1 1.4935(5 NiCr 180) Z 6 CN 18.09

Z 6 CN 18.10X 5 CrNi 18 9 X 5 CrNi 18 10

1.4301

1.10. OTEL PENTRU RULMENTISTAS 1456/1-80 NF

A 35-565-70SEW 350-53Marca Numar

RUL 1 100 C 6 100 Cr 6 1.3505RUL 2 - 100 CrMn 6 1.3520

1.11. OTEL REZISTENT LA UZURASTAS 11513-80 NF

A 35-551-72A 35-552-72


20 Mn 10 (20 M 5) 28 Mn 6 1.117040 Mn 10 (35 M 5) 40 Mn 4 1.1157

1.12. OTEL PENTRU TABLE GROASE DESTINATE RECIPIENTILOR SUB PRESIUNE, CU CONDITII SPECIALE DE CALITATE

STAS 11502-80 NFA 35-501-77A 35-201-75

SEW 089-70Marca Numar

RV 52 E 355 TTStE 36 1.0566R 55 E 420 TTStE 43 1.8912R 58 E 460 TTStE 47 1.891509 Mn 16 E 30-3

E 30-4- -

1.13. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA RIDICATA

STAS 2883/3-80 NFA 36-205-79A 36-206-78

DIN 17155-59Marca Numar

K 41 A 42 CP H II 1.0425K 47 A 48 CP 17 Mn 4 1.0481K 52 A 52 CP 19 Mn 5 1.048216 Mo 3 15 D 3 15 Mo 3 1.541514 CrMo 4 15 CD 4.05 13 CrMo 4 4 1.7335

1.14. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA SCAZUTA

STAS 2883/2-80 NFA 36-205-79A 36-208-79

DIN 17135-64SEW 089-70; SEW 680-70Marca Numar

R 37 A 37 AP ASt 35TTSt 35

1.03461.0356

R 44 A 48 APA 48 FP(05 N 285)

ASt 45TTSt 41TTStE 29

1.04361.04371.0488

R 52 A 52 APA 52 FP(05 N 355)

ASt 52TTStE 36

1.05771.0566

1.15. OTELURI PENTRU AUTOTURISMELE DACIA 1300STAS 11500/2-80 NF

A 35-551-72A 35-552-72A 35-571-74

DIN17200-6917210-6917221-72Marca Numar

38 Cr 05 38 C 2 38 Cr 2 1.7003OLC 42 XC 42 - -32 Cr 10 32 C 4 32 Cr 4 1.703337 Cr 10 38 C 4 37 Cr 4 1.7034

12 MoCr 10 - (13 CrMo 4) 1.733516 MoCr 10 16 CD 4

(18 CD 4)- -

20 MoCr 10 20 CD 4 - -30 MoCr 10 30 CD 4 - -33 MoCr 10 34 CD 4

(35 CD 4)34 MoCr 4 1.7220

20 NiCr 15 20 NC 6 (18 CrNi 8) 1.592035 MoCrNi 40 35 NCD 16 - -16 CrMn 12 16 MC 5 16 MnCr 5 1.7131X 61 SC 7 60 SiCr 7 1.0961

1.16. OTEL PENTU TEVI UTILIZATE LA TEMPERATURI RIDICATE

STAS 8184-80 NFA 49-811-73A 36-206-78

DIN17115-59Marca Numar

OLT 35 K TU 37- C St 35.8 1.0305OLT 45 K TU 48-C St 45.8 1.040516 Mo 3 15 D 3 15 Mo 3 1.541514 CrMo 4 15 CD 4.05 13 CrMo 4 4 1.733510 CrMo 10 10 CD 9.10 10 CrMo 9 10 1.738016 MoCr 50 - 12 CrMo 19 5 1.7362

1.17. OTEL CU GRANULATIE FINA PENTRU TABLE DESTINATE CONSTRUCTIILOR SUDATESTAS 9021-80 NF


OCS 44 - TTStE 29 1.0488OCS 52 E 355 TTStE 36 1.0566OCS 55 E 420 TTStE 43

WstE 431.89321.8912

OCS 58 E 460 TTSt E 47WstE 47

1.89151.8935

1.18. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI SCAZUTESTAS 10382-80 NF


OLT 35 R - TTSt 35 1.0356OLT 45 R - - -10 Ni 35 (3,5 N 355) 10 Ni 14 1.5637

1.19. OTEL PENTRU TABLE SI BENZI DESTINATE AMBUTISARIISTAS 9485-80 NF

A 36-401-69A 35-301-71


A 1 TC St 12 1.0330A 2 E St 13 1.0333A 3 (ES) St 14 1.0338A 3 Ck(STAS 11509-80)

3 C St W 24 1.0335

1.20. OTEL PENTRU TABLE SI BENZI LAMINATE LA RECE, DESTINATE CAROSERIILOR AUTOSTAS 10318-80 NF

A 36-401-69DIN 1623-72Marca Numar

A 4 E (St 13) 1.0333

A 5 ES (St 14) 1.03381.21. OTELURI REZISTENTE LA COROZIUNE

STAS 500/3-80 NFA 35-502-79

RCA 37 (E 24 W)RCA 52 (E 36 WB)

1.22. OTEL PENTRU AUTOMATESTAS 1350-80 NF


AUT 12 (10 F 1) (10 S 2) 1.0721AUT 20 - (22 S 20) 1.0724AUT 30 - (35 S 20) 1.0726AUT 40 M (45 MF 6) (45 S 20) 1.0727

1.23. OTEL PENTRU PINIOANESTAS 11512-80 NF

A 35-551-72A 35-552-72


17 CrNiMo 6 18 NCD 6 17 CrNiMo 6 1.65871.24. OTEL PENTRU ORGANE DE ASAMBLARE

STAS 11511-80 NFA 35-551-72A 35-552-72

DIN (norma tehnica interna)Marca Numar

20 MnB 5 20 MB 5 20 MnB 3 1.55071.25. OTEL PENTRU TEVI FARA SUDURA, DE UZ GENERAL

STAS 8183-80 NF DIN 1629-61Marca Numar

OLT 35 St 35 1.0308OLT 45 St 45 1.0408OLT 65 - -

1.26. OTEL PENTRU SUPAPELE MOTOARELOR CU ARDERE INTERNASTAS 11311-80 NF

A 35-579-70DIN (dupa norma interna)Marca Numar

45 SiCr 85 Z 45 CS 9 (X 45 CrSi 9 3) 1.47181.27. OTEL PENTRU SUPAPE DE EVACUARE

STAS 11524-80 NFA 35-579-70

DIN (dupa norma interna)Marca Numar

45 SiCr 95 45 CS 9 X 45 CrSi 9 3 1.471880 SiNiCr 200 Z 80 CSN 20.02 X 80 CrNiSi 20 1.474753 NNiMnCr 210 Z 52 CMN 21.09 X 53 CrMnNiN 21 9 1.4871

1.28. OTEL TERMOREZISTENT PENTRU ORGANE DE ASAMBLARESTAS 11512-80 NF


24 VMoCr 12 28 CDV 5.08 24 CrMoV 5 5 1.773312 MoCr 90 - X 12 CrMo 9 1 1.7386

2. OTELURI TURNATERecomandari de utilizare :· Corespondenta marcilor de oteluri turnate este orientativa si in conformitate cu STAS R 4400/2-88,· Corespondenta indicata este aproximativa si data cu titlu informativ. Ea este stabilita pe baza : compozitiei chimice, caracteristicilor mecanice si a conditiilor de utilizare.2.1. OTEL SLAB ALIAT SI ALIAT TURNAT IN PIESE

STAS 1773-82 NFA 32-054-78A 32-055-76

TGL14395-85

T 20 Mn 14 20 M 6-M GS-20 Mn 6T 35 Mn 14 30 M 6-M GS-35 Mn 6T 40 Mn 11 - GS-45 Mn 4T 30 SiMn 12 FC-M -T 34 MoCr 09 25 CD 4-M GS-30 CrMo 4T 35 MoCrNi 08 - -T 26 VSiMn 14 30 MV6-M -T 20 TiMn 12 - -T 35 SiCrMn 11 - GS-40 MnCrSi 3T 30 MoCrNi 14 30 NCD 8-M GS-30 CrNiMo 6 T 14 VMoCuNi 16 - -T 40 VMn 17 - -poansoane, lame ascutite : 50 CD 4-M piese foarte solicitate la frecare : 32 NCD 14- M matrite forja, scule de taiere si calibrare :

35 cdv 5-M

piese foarte solicitate cu duritate foarte ridicata :

Z160CDV 12- M

2.2. OTEL AUSTENITIC MANGANOS TURNAT IN PIESESTAS 3718-87 NF


T 105 Mn 120 -T 130 Mn 135 Z 120 M 12-M G-X 120 Mn 12T 120 CrMn 130 Z 120 MC 12-MT 100 NiMn 130 Z 100 MN 13.4-MT 100 MoMn 130 Z 110 MD 12.1-MT 35 NiCr 260 (Z 40 CN 25.20-M) G-X 40 CrNiSi 25 12 1.4837T 25 NiCr 250 G-X 15 CrNi 25 20 1.4840T 35 CrNi 370 G-X 40 CrNiSi 36 18 1.4865T 12 MoNiCr 210 - -2.3. OTELURI TURNATE IN PIESE PENTRU ARMATURISTAS 9277-84 NF

A 32-055-76A 32-056-84


OTA 20 A 42 C-M GS-C 25 1.0619OTA 40Mn13 - - -OTA 30VMn13 - - -OTA 17MoCr13 15 CD 5.05-M GS-18CrMo9 10 1.7379OTA 23VWMoCr120 - G-X22CrMoV12 1 1.4931OTA 10NbMoNiCr170 Z 4 CNDNb 18.12-M G-X5CrNiMoNb18.10 1.4581OTA 10TiMoNiCr170 - - -2.4. OTEL CARBON, SLAB ALIAT SI MEDIU ALIAT REZISTENT LA TEMPERATURI RIDICATE, TURNAT IN PIESESTAS 12404-85 NF


T 21 A 42 C-M GS-C 25 1.0619T 16 Mo 5 - GS-22 Mo 4 1.5419

T 16 MoCr 11 15 CD 4.05-M GS-17 CrMo 5 5 1.7357T 14 MoVCr 6 - - -T 21 VMoCr 10 NCDV 4.10-M - -T 17 VMoCr 14 15 CDV 9.10-M GS-17 CrMoV 5 11 1.7706T 15 MoWVCr 12 - - -

Notatii utilizate:· STAS -standard de stat Romania· NF -norma Franta· DIN, SEW - norme GermaniaSimbolizarea elementelor chimice utilizate :

Denumirea inl. romana

Simbolul dupa STAS

Simbol dupa NF Simbol dupaDIN, SEW

Aluminiu Al A AlNichel Ni N NiMolibden Mo D MoCrom Cr C CrCupru Cu U CuStaniu Sn E SnSulf (fosfor) S F SMangan Mn M MnPlumb Pb Pb PbAzot (nitrogen) N Az NSiliciu Si S SiTitan Ti T TiTugsten W W WVanadiu V V VZinc Zn Z ZnZirconiu Zr ZR ZrBor B B BNiobiu Nb Nb NbCobalt Co K

3. FONTE3.1. FONTE CU GRAFIT LAMELARSR ISO 185-94 Simbol vechi

STAS 568-82NF DIN

Marca RmN/mm2

Marca Numar

100 100 Fc 100 Ft 10 D GG-10 0.6010150 150 Fc 150 Ft 15 D GG-15 0.6015200 200 Fc 200 Ft 20 D GG-20 0.6020250 250 Fc 250 Ft 25 D GG-25 0.6025300 300 Fc 300 Ft 30 D GG-30 0.6030350 350 Fc 350 Ft 35 D GG-35 0.6035- 400 Fc 400 Ft 40 D GG-40 0.6040

FGL 175HB*FGL 215HB*FGL 240HB*

*Fonte prevazute pe echipamente RENAULT (E01.41.050.N):

3.2. FONTE CU GRAFIT NODULAR (SFEROIDAL)SR ISO 5922-95 Simbol vechi NF DIN

STAS 6071-82Marca RmN/mm2

A%

Marca Numar

Ft GjS 900-2 900 2 - - - -800-2 800 2 Fgn 800-3 FGS 800.2 GGG-80 0.7080700-2 700 2 Fgn 700-2 FGS 700.2 GGG-70 0.7070600-3 600 3 Fgn 600-2 FGS 600.3 GGG-60 0.7060- - FGS 600-3A*500-7 500 7 Fgn 500-7 FGS 500.7 GGG-50 0.7050450-10 450 10 Fgn 450-5 - (GGG-40.3) 0.7043400-15 400 15 - (FGS 400.12) GGG-40 0.7040400-18 350 18 - - - -- - FGS 400-18A*350-22 350 22 - (FGS 370.17) GGG-35.3 0.7033

*Fonte prevazute pe echipamente RENAULT (E01.45.030.N) :

3.3. FONTE MALEABILESR ISO 5922-95 Simbol

vechi569-79

NF DINMarca Rm

N/mm2A%

Tip Marca Numar

W 35-04 350 4 cuinimaalba

Fma 350 (MB 35.7) GTW-35 0.8035W 38-12 380 12 - - GTW-S38 0.8038W 40-05 400 5 Fma 400 (MB 40.10) GTW-40 0.8040W 45-07 450 7 - - GTW-45 0.8045B 30-06 300 6 cu

inimaneagra

Fmn 300 - - -B 32-12 320 12 Fmn 320 - - -B 35-10 350 10 Fmn 350 MN 35.10 GTS-35 0.8135P 45-06 450 6 perlitica Fmp 450 GTS-45 0.8145P 50-05 500 5 Fmp 500 - - -P 55-04 550 4 Fmp 550 GTS-55 0.8155P 60-03 600 3 Fmp 600 - - -P 65-02 650 2 Fmp 650 GTS-65 0.8165P 70-02 700 2 Fmp 700 MP 70.2 GTS-70 0.8170P 80-01 800 1 -

3.4. FONTE CU GRAFIT NODULAR CU STRUCTURA BAINITICASR ISO 13169-94 Simbol

STASvechi

Marca RmN/mm2

A%

HB

FgnB 800 800 10 260-320 nu existaFgnB 900 900 8 280-340FgnB 1000 1000 5 300-380FgnB 1100 1100 3 360-420FgnB 1200 1200 2 380-450FgnB 1400 1400 - 450-550

GHID CORESPONDENTA OTELURI