GHID

PRIVIND CORESPONDENTA MATERIALELOR

(valabil pentru mentenanta mijloacelor)

F115.20-04-002RA, vers 01

Uz intern : AUTOMOBILE DACIA

Data elaborarii: martie 2004

Elaborat : Vasile BAIASU

CUPRINS

1. OTELURI LAMINATE SI TRASE

1.1. OTEL DE UZ GENERAL PENTRU CONSTRUCTII

1.2. OTEL CARBON DE CALITATE PENTRU TRATAMENT TERMIC, DESTINAT CONSTRUCTIEI DE MASINI

1.3. OTEL PENTRU ARCURI

1.4. OTEL ALIAT PENTRU TRATAMENT TERMIC IN CONSTRUCTIA DE MASINI

1.5. OTEL RAPID PENTRU SCULE

1.6. OTEL PENTRU SCULE

1.7. OTEL ALIAT PENTRU SCULE

1.8. OTEL REZISTENT LA COROZIUNE SI 14414p1519o REFRACTAR, PRELUCRAT LA CALD

1.9. OTEL INOXIDABIL SI REFRACTAR

1.10. OTEL PENTRU RULMENTI

1.11. OTEL REZISTENT LA UZURA

1.12. OTEL PENTRU AUTOTURISME DACIA

1.13. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA RIDICATA

1.14. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA SI SCAZUTA

1.15. OTEL PENTRU AUTOTURISME DACIA

1.16. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI RIDICATE

1.17. OTEL CU GRANULATIE FINA PENTRU TABLE DESTINATE CONSTRUCTIILOR SUDATE

1.18. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI SCAZUTE

1.19. OTEL PENTRU TABLE SI BENZI DESTINATE AMBUTISARII

1.20. OTEL PENTRU TABLE SI BENZI LAMINATE LA RECE DESTINATE CAROSERIILOR AUTO

1.21. OTEL REZISTENT LA COROZIUNE

1.22. OTEL PENTRU AUTOMATE

1.23. OTEL PENTRU PINIOANE

1.24. OTEL PENTRU ORGANE DE ASAMBLARE

1.25. OTEL PENTRU TEVI FARA SUDURA, DE UZ GENERAL

1.26. OTEL PENTRU SUPAPELE MOTOARELOR CU ARDERE INTERNA

1.27. OTEL PENTRU SUPAPE EVACUARE

1.28. OTEL TERMOREZISTENT PENTRU ORGANE DE SAMBLARE

2. OTELURI TURNATE

2.1. OTEL SLAB ALIAT SI ALIAT TURNAT IN PIESE

2.2. OTEL AUSTENITIC MANGANOS TURNAT IN PIESE

2.3. OTEL TURNAT IN PIESE PENTRU ARMATURI

2.4. OTEL CARBON, SLAB ALIAT REZISTENT LA TEMPERATURI RIDICATE, TURNAT IN PIESE

3. FONTE

3.1. FONTE CU GRAFIT LAMELAR

3.2. FONTE CU GRAFIT NODULAR

3.3. FONTE MALEABILE

3.4. FONTE CU GRAFIT NODULAR CU STRUCTURA BAINITICA

1. oteluri

Recomandari de utilizare:

• Corespondenta marcilor de oteluri laminate sau trase este in conformitate cu STAS R 4400/1-80.

• Corespondenta indicata este aproximativa si data cu titlu informativ. Ea este stabilita pe baza : compozitiei chimice, caracteristicilor mecanice si a conditiilor de utilizare.

• Pentru marcile straine indicate intre paranteze corespondenta stabilita este foarte larga.

1.1. OTEL DE UZ GENERAL PENTRU CONSTRUCTII

STAS 500/2-80 NF

A 35-501-77

DIN 17100

Marca Numar

OL 34.1 A 34-1 USt 34-11.0055

OL 37.1

OL 37.2

OL 37.2k

OL 37.3

OL 37.4

E 24-1

E 24-2 (S235JR)

E 24-2NE

E 24-3

E 24-4

USt 37-1

USt 37-2

RSt 37-2

St 37-3

St 37-3

1.0065

1.0036

1.0038

1.0116

1.0116

OL 42.1

OL 42.1k

OL 42.2

OL 42.2k

OL 42.3

-

E 26-1

E 26-1NE

E 26-2

E 26-2NE

E 26-3

E 26-4

USt 42-1

RSt 42-1

USt 42-2

RSt 42-2

St 42-3

St 42-3

1.0075

1.0077

1.0040

1.0042

1.0136

1.0136

OL 44.2(k)

OL 44.3(k)

OL 44.4(k)

E 30-2

E 30-3

E 30-4

RSt 46-2

St 46-3

St 46-3

1.0477

1.0483

1.0483

OL 52.2(k)

OL 52.3(k)

OL 52.4(k)

E 36-2

E 36-3

E 36-4

-

St 52-3

St 52-3

-

1.0570

1.0570

OL 50(k) A 50-2 St 50-2 1.0050

OL 60(k) A 60-2 St 60-2 1.0060

OL 70(k) A 70-2 St 70-2 1.0070

OL 30 A 33-1

A 33-2

St 33-1

St 33-2

1.0033

1.0035

1.2. OTEL CARBON DE CALITATE PENTRU TRATAMENT TERMIC, DESTINAT CONSTRUCTIEI DE MASINI

STAS 880-80NF

A 35-551-72

A 35-552-72

DIN

17200-69

17210-69

Marca Numar

OLC 10

OLC 10 X

CC 10 , (AF 34 C 10)*

XC 10

C 10

Ck 10

1.0301

1.1121

OLC 15

OLC 15 X

AF 37 C 12)*

XC 18, (XC 15)

C 15

Ck 15

1.0401

1.1141

OLC 20 CC 20 - -

OLC 25

OLC 25 X

(AF 42 C 20)*

XC 25, (XC 18)

C22

Ck 22

1.0402

1.1151

OLC 35

OLC 35 X

CC 35, (AF 55 C 35)*

XC 38, (XC 35), (XC 32)

C 35

Ck 35

1.0501

1.1181

OLC 45

OLC 45 X

CC 45,(AF 65 C 45)*

XC 48, (XC 45), (XC 42)

C 45

Ck 45

1.0503

1.1191

OLC 55

OLC 55 X

XC 55, (XC 54) C 55

Ck 55

1.0535

1.1203

OLC 60

OLC 60X

(AF 70 C 55)*

XC 60, (XC 65)

C 60

Ck 60

1.0601

1.1221

*simbolizare veche

1.3. OTEL PENTRU ARCURI

STAS 795-80 NF

A 35-551-72

A 35-552-72

A 35-571-74

DIN

17221-72

17222-72

Marca Numar

OLC 55 A XC 55 Ck 551.1203

OLC 65 A

(OLC 66 S

STAS 8371-80)

XC 68 (XC 65) Ck 67 1.1231

OLC 75 A XC 75 Ck 75 1.1248

OLC 85 A - Ck 85 1.1269

51 Si 17 A 51 S 7 51 Si 7 1.0903

40 Si 17 A (45 S 7) - -

51 VCr 11 A 50 CV 4 50CrV 4 1.8159

56 Si 17 A 55 S 7 55 Si 7 1.0904

60 Si 15 A - 60SiCr7 1.7108

65 S 2 WA

(STAS 11514-80)

- - -

1.4. OTEL ALIAT PENTRU TRATAMENT TERMIC IN CONSTRUCTIA DE MASINI

STAS 791-80 NF

A 35-551-72

A 35-552-72

A 35-571-74

DIN

17210-69

17200-69

Marca Numar

15 Cr 08- (15 Cr 3) 1.7015

18 MnCr 1016 MC 5

16 MnCr 5 1.7131

21 MoMnCr 12 (18 CD 4) - -

18 MoCrNi 1318 NCD 6

18 CND 6

17 CrNiMo 6 1.6587

13 CrNi 30 (14 NC 11)

(16 NC 11)

(14 NiCr 10) 1.5732

20 MoNi 35 - - -

21 TiMnCr 12 - - -

28 TiMnCr 12 - - -

35 Mn 16 - - -

65 Mn 10 - 65 Mn 4 1.2817

35 MnSi 12 - 37 MnSi 5 1.5122

40 Cr 10 42 C 4 41 Cr 4 1.7035

40 BCr 10 - - -

33 MoCr 11 34 CD 4

(35 CD 4)

34 CrMo 4 1.7220

41 MoCr 11 (38 CD 4)

40 CD 4

42 CD 4

42 CrMo 4 1.7225

50 VCr 11 50 CV 4 50 CrV 4 1.8159

34 MoCrNi 15 (35 NCD 6) 34 CrNiMo 8 1.6582

30 MoCrNi 20 30 CND 8

30 NCD 8

30 CrNiMo 8 1.6580

38 MoCrAl 09 (40 CAD 6.12) (34 CrAlMo 5)

(41 CrAlMo 7)

1.8507

1.8509

41 CrNi 12 (30 NC 12) (31 NiCr 14) 1.5752

18 CrNi 20 20 NC 6 18 CrNi 8 1.5920

1.5. OTEL RAPID DE SCULE

STAS 7382-80 NF

A 35-590-78

SEW

320-69

Marca Numar

Rp 1- - -

Rp 2 Z 80 WKCV 18.05.04.01HS 18-1-2-5

1.3255

Rp 3 (Z80 WCV 18.04.01) HS 18-0-1 1.3355

Rp 5 Z 85 WDCV 06.05.04.02 HS 6-5-2C 1.3343

Rp 9 - HS 3-3-2 1.3333

Rp 10 Z 85 DCWV 08.04.02.02 HS 2-9-1 1.3346

- Z 110 WKDV 07.05.04.02 HS 7-4-2-5

- Z 120 WDV 06 HS 6-5-3

- Z 150 WKV 12 HS 12-4-5-5

- Z 110 DKWV 09.08.02.01 HS 2-9-1-8

- Z 160 WDV 06 HS 6-5-3

- Z 110 DK 09 (lame de forma, scule GLEASON)

1.6. OTEL PENTRU SCULE

STAS 1700-80 NF

A 35-590-78

SEW

150-71

Marca Numar

OSC 7 Y1 70(C 67 W3) 1.1744

OSC 8 Y1 80

Y1 90

C 80 W 1

C 80 W 2

1.1525

1.1625

OSC 10 Y1 105 (C 105 W 1)

(C 105 W 2)

1.1545

1.1645

OSC 11 - C 110 W 2 1.1654

OSC 13 -

-

-

(C 125 W 1)

(C 125 W 2)

(C 135 W 2)

1.1560

1.1663

1.1673

1.7. OTEL ALIAT PENTRU SCULE

STAS 3611-80NF

A 35-590-78

SEW 200-69

SEW 250-70

Marca Numar

MCV 14 105 WC 13 105 WCr 61.2419

VM 18 90 MV 8 90 MnCrV 8 1.2842

CW 20(105 WC 13) (105 WCr 6) 1.2419

C 120 Z 200 C 12 X 210 Cr 12 1.2080

VMoC 120 Z 160 CDV 12 X 153 CrMoV 12 1.2601

CV 06 - 115 CrV 3 1.2210

VCW 85 Z 30 WCV 9 X 30 WCrV9 3 1.2581

MoCN 15 - 55 NiCrMoV 6 1.2713

VMoCN 17 55 NCDV 7 56 NiCrMoV 7 1.2714

MoVC 30 32 DCV 5 X 32 CrMoV 3 3 1.2365

- 35 CDV 5 X 100 CrMoV 5

MoVC 50.10 Z 38 CDV 5 X 37 CrMoV 5 1 1.2343

MoVC 50.13 Z 40 CDV 5 X 40 Cr MoV 5 1 1.2344

MoWC 53 - X 37 CrMoW 5 1 1.2606

VSCW 20 - 45 WCrV 7 1.2542

1.8. OTEL REZISTENT LA COROZIUNE SI REFRACTAR, PRELUCRAT LA CALD

STAS 3583-80NF

A 35-572-75

A 35-578-70

DIN 17440-72

SEW 470-76

Marca Numar

12 Cr 130Z 12 C 13 X 10 Cr 13 1.4006

20 Cr 130 Z 20 C 13 X 20 Cr 13 1.4021

30 Cr 130 Z 30 C 13 X 30 Cr 13 1.4028

40 Cr 130 - X 40 Cr 13 1.4034

8 (Ti)Cr 170 Z 8 C 17 X 8 Cr 17

X 6 Cr Ti 17

1.4016

1.4510

12 NiCr 180 (Z 10 CN 18.09) X 12 CrNi 18 8 1.4300

10 TiNiCr 180

(STAS 10322-80)

Z 6 CNT 18.10 X 10 CrNiTi 18 9 1.4541

10 TiMoNiCr 175 Z 6 CNDT 17.12 X 10 CrNiMoTi 18 10 1.4571

15 SiNiCr 250

(Cr 25 Ni 20

STAS 11510-80)

Z 12 CNS 25.20 X 15 CrNiSi 25 20 1.4841

1.9. OTEL INOXIDABIL SI REFRACTAR

STAS 11523-80 NF

A 35-572-75

A 35-576-75

A 35-578-70

A 35-583-75

DIN 1770-72

SEW 400-73

SEW 470-76

SEW 670-69

Marca Numar

7 AlCr 130 Z 6 CA 13

X 7 CrAl 13 1.4002

22 NiCr 170 Z 15 CN 16.02 X 22 CrNi 17 1.4057

90 VmoCr 180 Z 100 CD 17 X 90 CrMoV 18 1.4112

35 MoCr 165 - X 35 CrMo 17 1.4122

2 NiCr 185 Z 2 CN 18.09

Z 2 CN 18.10

X 2 CrNi 18 9 1.4306

2 MoNiCr 175 Z 2 CND 17.12 X 2 CrNiMo 18 12 1.4435

2 CuMoCrNi 250 Z 1 NCDU 25.20 (X 2 NiCrMoCu 25 21) 1.4536

10 AlCr 240 Z 10 CAS 24 X 10 CrAl 24 1.4762

15 SiNiCr 200 Z 15 CNS 20.15 X 15 CrNiSi 20 12 1.4828

12 NiCr 250 Z 12 CN 25.20 X 12 CrNi 25 21 1.4845

2 NiCr 250 Z 2 CNNb 25.20 (X 5 CrNi 25 21) 1.4335

12 SiCrNi 360 Z 12 NCS 35.16 X 12 NiCrSi 36 16 1.4864

40 SiCrNi 380 - X 40 NiCrSi 36 16 1.4865

10 TiAlCrNi 320 - X 10 NiCrAlTi 32 20 1.4876

12 TiNiCr 180 Z 6 CNT 18.12 B X 12 CrNiTi 18 9 1.4878

19 MoCr 120 - X 19 CrNiTi 12 1 1.4921

20 VWMoCr 120 - X 20 CrMoWV 12 1 1.4935

(5 NiCr 180) Z 6 CN 18.09

Z 6 CN 18.10

X 5 CrNi 18 9

X 5 CrNi 18 10

1.4301

1.10. OTEL PENTRU RULMENTI

STAS 1456/1-80NF

A 35-565-70

SEW 350-53

Marca Numar

RUL 1100 C 6 100 Cr 6 1.3505

RUL 2 - 100 CrMn 6 1.3520

1.11. OTEL REZISTENT LA UZURA

STAS 11513-80 NF

A 35-551-72

A 35-552-72

DIN

17200-69

17115-72

Marca Numar

20 Mn 10(20 M 5) 28 Mn 6 1.1170

40 Mn 10 (35 M 5) 40 Mn 4 1.1157

1.12. OTEL PENTRU TABLE GROASE DESTINATE RECIPIENTILOR SUB PRESIUNE, CU CONDITII SPECIALE DE CALITATE

STAS 11502-80 NF

A 35-501-77

A 35-201-75

SEW 089-70

Marca Numar

RV 52E 355 TTStE 36 1.0566

R 55 E 420 TTStE 43 1.8912

R 58 E 460 TTStE 47 1.8915

09 Mn 16 E 30-3

E 30-4

- -

1.13. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB PRESIUNE, PENTRU TEMPERATURA AMBIANTA RIDICATA

STAS 2883/3-80 NF

A 36-205-79

A 36-206-78

DIN 17155-59

Marca Numar

K 41A 42 CP H II 1.0425

K 47 A 48 CP 17 Mn 4 1.0481

K 52 A 52 CP 19 Mn 5 1.0482

16 Mo 3 15 D 3 15 Mo 3 1.5415

14 CrMo 4 15 CD 4.05 13 CrMo 4 4 1.7335

1.14. OTEL PENTRU TABLE DESTINATE CAZANELOR SI RECIPIENTELOR SUB

PRESIUNE, PENTRU TEMPERATURA AMBIANTA SCAZUTA

STAS 2883/2-80NF

A 36-205-79

A 36-208-79

DIN 17135-64

SEW 089-70; SEW 680-70

Marca Numar

R 37A 37 AP ASt 35

TTSt 35

1.0346

1.0356

R 44 A 48 AP

A 48 FP

(05 N 285)

ASt 45

TTSt 41

TTStE 29

1.0436

1.0437

1.0488

R 52 A 52 AP

A 52 FP

(05 N 355)

ASt 52

TTStE 36

1.0577

1.0566

1.15. OTELURI PENTRU AUTOTURISMELE DACIA 1300

STAS 11500/2-80NF

A 35-551-72

A 35-552-72

A 35-571-74

DIN

17200-69

17210-69

17221-72

Marca Numar

38 Cr 0538 C 2 38 Cr 2 1.7003

OLC 42 XC 42 - -

32 Cr 10 32 C 4 32 Cr 4 1.7033

37 Cr 10 38 C 4 37 Cr 4 1.7034

12 MoCr 10 - (13 CrMo 4) 1.7335

16 MoCr 10 16 CD 4

(18 CD 4)

- -

20 MoCr 10

20 CD 4 - -

30 MoCr 10 30 CD 4 - -

33 MoCr 10 34 CD 4

(35 CD 4)

34 MoCr 4 1.7220

20 NiCr 15 20 NC 6 (18 CrNi 8) 1.5920

35 MoCrNi 40 35 NCD 16 - -

16 CrMn 12 16 MC 5 16 MnCr 5 1.7131

X 61 SC 7 60 SiCr 7 1.0961

1.16. OTEL PENTU TEVI UTILIZATE LA TEMPERATURI RIDICATE

STAS 8184-80 NF

A 49-811-73

A 36-206-78

DIN

17115-59

Marca Numar

OLT 35 KTU 37- C St 35.8 1.0305

OLT 45 K TU 48-C St 45.8 1.0405

16 Mo 3 15 D 3 15 Mo 3 1.5415

14 CrMo 4 15 CD 4.05 13 CrMo 4 4 1.7335

10 CrMo 10 10 CD 9.10 10 CrMo 9 10 1.7380

16 MoCr 50 - 12 CrMo 19 5 1.7362

1.17. OTEL CU GRANULATIE FINA PENTRU TABLE DESTINATE CONSTRUCTIILOR SUDATE

STAS 9021-80NF

A 36-201-75

SEW 089-70

Marca Numar

OCS 44- TTStE 29 1.0488

OCS 52 E 355 TTStE 36 1.0566

OCS 55 E 420 TTStE 43

WstE 43

1.8932

1.8912

OCS 58 E 460 TTSt E 47

WstE 47

1.8915

1.8935

1.18. OTEL PENTRU TEVI UTILIZATE LA TEMPERATURI SCAZUTE

STAS 10382-80NF

A 36-208-79

SEW 680-70

Marca Numar

OLT 35 R- TTSt 35 1.0356

OLT 45 R - - -

10 Ni 35 (3,5 N 355) 10 Ni 14 1.5637

1.19. OTEL PENTRU TABLE SI BENZI DESTINATE AMBUTISARII

STAS 9485-80NF DIN 1623-72

A 36-401-69

A 35-301-71

Marca Numar

A 1 TC St 12 1.0330

A 2 E St 13 1.0333

A 3 (ES) St 14 1.0338

A 3 Ck

(STAS 11509-80)

3 C St W 24 1.0335

1.20. OTEL PENTRU TABLE SI BENZI LAMINATE LA RECE, DESTINATE CAROSERIILOR AUTO

STAS 10318-80NF

A 36-401-69

DIN 1623-72

Marca Numar

A 4E (St 13) 1.0333

A 5 ES (St 14) 1.0338

1.21. OTELURI REZISTENTE LA COROZIUNE

STAS 500/3-80NF

A 35-502-79

RCA 37 (E 24 W)

RCA 52 (E 36 WB)

1.22. OTEL PENTRU AUTOMATE

STAS 1350-80 NF

A 35-562-78

DIN 1651-70

Marca Numar

AUT 12(10 F 1) (10 S 2) 1.0721

AUT 20 - (22 S 20) 1.0724

AUT 30 - (35 S 20) 1.0726

AUT 40 M (45 MF 6) (45 S 20) 1.0727

1.23. OTEL PENTRU PINIOANE

STAS 11512-80 NF

A 35-551-72

A 35-552-72

DIN 17210-69

Marca Numar

17 CrNiMo 618 NCD 6 17 CrNiMo 6 1.6587

1.24. OTEL PENTRU ORGANE DE ASAMBLARE

STAS 11511-80NF

A 35-551-72

A 35-552-72

DIN (norma tehnica interna)

Marca Numar

20 MnB 520 MB 5 20 MnB 3 1.5507

1.25. OTEL PENTRU TEVI FARA SUDURA, DE UZ GENERAL

STAS 8183-80 NF DIN 1629-61

MarcaNumar

OLT 35 St 35 1.0308

OLT 45 St 45 1.0408

OLT 65 - -

1.26. OTEL PENTRU SUPAPELE MOTOARELOR CU ARDERE INTERNA

STAS 11311-80 NF

A 35-579-70

DIN (dupa norma interna)

Marca Numar

45 SiCr 85 Z 45 CS 9 (X 45 CrSi 9 3) 1.4718

1.27. OTEL PENTRU SUPAPE DE EVACUARE

STAS 11524-80 NF

A 35-579-70

DIN (dupa norma interna)

Marca Numar

45 SiCr 9545 CS 9 X 45 CrSi 9 3 1.4718

80 SiNiCr 200 Z 80 CSN 20.02 X 80 CrNiSi 20 1.4747

53 NNiMnCr 210 Z 52 CMN 21.09 X 53 CrMnNiN 21 9 1.4871

1.28. OTEL TERMOREZISTENT PENTRU ORGANE DE ASAMBLARE

STAS 11512-80 NF

A 35-558-69

DIN 17240-76

Marca Numar

24 VMoCr 1228 CDV 5.08 24 CrMoV 5 5 1.7733

12 MoCr 90 - X 12 CrMo 9 1 1.7386

2. OTELURI TURNATE

Recomandari de utilizare :

• Corespondenta marcilor de oteluri turnate este orientativa si in conformitate cu STAS R 4400/2-88,

• Corespondenta indicata este aproximativa si data cu titlu informativ. Ea este stabilita pe baza : compozitiei chimice, caracteristicilor mecanice si a conditiilor de utilizare.

2.1. OTEL SLAB ALIAT SI ALIAT TURNAT IN PIESE

STAS 1773-82 NF

A 32-054-78

A 32-055-76

TGL

14395-85

T 20 Mn 1420 M 6-M GS-20 Mn 6

T 35 Mn 14 30 M 6-M GS-35 Mn 6

T 40 Mn 11 - GS-45 Mn 4

T 30 SiMn 12 FC-M -

T 34 MoCr 09 25 CD 4-M GS-30 CrMo 4

T 35 MoCrNi 08 - -

T 26 VSiMn 14 30 MV6-M -

T 20 TiMn 12 - -

T 35 SiCrMn 11 - GS-40 MnCrSi 3

T 30 MoCrNi 14 30 NCD 8-M GS-30 CrNiMo 6

T 14 VMoCuNi 16 - -

T 40 VMn 17 - -

poansoane, lame ascutite : 50 CD 4-M

piese foarte solicitate la frecare :

32 NCD 14- M

matrite forja, scule de taiere si calibrare :

35 cdv 5-M

piese foarte solicitate cu duritate foarte ridicata :

Z160CDV 12- M

2.2. OTEL AUSTENITIC MANGANOS TURNAT IN PIESE

STAS 3718-87NF

A 32-058-84

DIN 17445-73

Marca Numar

T 105 Mn 120-

T 130 Mn 135 Z 120 M 12-M G-X 120 Mn 12

T 120 CrMn 130 Z 120 MC 12-M

T 100 NiMn 130Z 100 MN 13.4-M

T 100 MoMn 130 Z 110 MD 12.1-M

T 35 NiCr 260 (Z 40 CN 25.20-M) G-X 40 CrNiSi 25 12 1.4837

T 25 NiCr 250 G-X 15 CrNi 25 20 1.4840

T 35 CrNi 370 G-X 40 CrNiSi 36 18 1.4865

T 12 MoNiCr 210 - -

2.3. OTELURI TURNATE IN PIESE PENTRU ARMATURI

STAS 9277-84NF

A 32-055-76

A 32-056-84

DIN 17245-77

Marca Numar

OTA 20 A 42 C-M GS-C 25 1.0619

OTA 40Mn13 - - -

OTA 30VMn13 - - -

OTA 17MoCr13 15 CD 5.05-M GS-18CrMo9 10 1.7379

OTA 23VWMoCr120 - G-X22CrMoV12 1 1.4931

OTA 10NbMoNiCr170 Z 4 CNDNb 18.12-M G-X5CrNiMoNb18.10 1.4581

OTA 10TiMoNiCr170 - - -

2.4. OTEL CARBON, SLAB ALIAT SI MEDIU ALIAT REZISTENT LA TEMPERATURI RIDICATE, TURNAT IN PIESE

STAS 12404-85 NF

A 32-055-85

DIN 17245-75

Marca Numar

T 21 A 42 C-M GS-C 25 1.0619

T 16 Mo 5 - GS-22 Mo 4 1.5419

T 16 MoCr 11 15 CD 4.05-M GS-17 CrMo 5 5 1.7357

T 14 MoVCr 6 - - -

T 21 VMoCr 10 NCDV 4.10-M - -

T 17 VMoCr 14 15 CDV 9.10-M GS-17 CrMoV 5 11 1.7706

T 15 MoWVCr 12 - - -

Notatii utilizate:

• STAS –standard de stat Romania

• NF –norma Franta

• DIN, SEW – norme Germania

Simbolizarea elementelor chimice utilizate :

Denumirea in

l. romana

Simbolul dupa STAS

Simbol dupa NF

Simbol dupa

DIN, SEW

Aluminiu Al A Al

Nichel Ni N Ni

Molibden Mo D Mo

Crom Cr C Cr

Cupru Cu U Cu

Staniu Sn E Sn

Sulf (fosfor) S F S

Mangan Mn M Mn

Plumb Pb Pb Pb

Azot (nitrogen) N Az N

Siliciu Si S Si

Titan Ti T Ti

Tugsten W W W

Vanadiu V V V

Zinc Zn Z Zn

Zirconiu Zr ZR Zr

Bor B B B

Niobiu Nb Nb Nb

Cobalt Co K

3. FONTE

3.1. FONTE CU GRAFIT LAMELAR

SR ISO 185-94Simbol vechi

STAS 568-82

NF DIN

Marca Rm

N/mm2

Marca Numar

100 100 Fc 100 Ft 10 D GG-10 0.6010

150 150 Fc 150 Ft 15 D GG-15 0.6015

200 200 Fc 200 Ft 20 D GG-20 0.6020

250 250 Fc 250 Ft 25 D GG-25 0.6025

300 300 Fc 300 Ft 30 D GG-30 0.6030

350 350 Fc 350 Ft 35 D GG-35 0.6035

- 400 Fc 400 Ft 40 D GG-40 0.6040

FGL 175HB*

FGL 215HB*

FGL 240HB*

*Fonte prevazute pe echipamente RENAULT (E01.41.050.N):

3.2. FONTE CU GRAFIT NODULAR (SFEROIDAL)

SR ISO 5922-95 Simbol vechi

NF DIN

STAS 6071-82

Marca Rm

N/mm2

A

%

Marca Numar

Ft GjS 900-2 900 2 - - - -

800-2 800 2 Fgn 800-3 FGS 800.2 GGG-80 0.7080

700-2 700 2 Fgn 700-2 FGS 700.2 GGG-70 0.7070

600-3 600 3 Fgn 600-2 FGS 600.3 GGG-60 0.7060

- - FGS 600-3A*

500-7 500 7 Fgn 500-7 FGS 500.7 GGG-50 0.7050

450-10 450 10 Fgn 450-5 - (GGG-40.3) 0.7043

400-15 400 15 - (FGS 400.12) GGG-40 0.7040

400-18 350 18 - - - -

- - FGS 400-18A*

350-22 350 22 - (FGS 370.17) GGG-35.3 0.7033

*Fonte prevazute pe echipamente RENAULT (E01.45.030.N) :

3.3. FONTE MALEABILE

SR ISO 5922-95 Simbol

vechi

569-79

NF DIN

Marca Rm

N/mm2

A

%

Tip Marca Numar

W 35-04 350 4 cu Fma 350 (MB 35.7) GTW-35 0.8035

inima

alba

W 38-12 380 12 - - GTW-S38 0.8038

W 40-05 400 5 Fma 400 (MB 40.10) GTW-40 0.8040

W 45-07 450 7 - - GTW-45 0.8045

B 30-06 300 6 cu

inima

neagra

Fmn 300 - - -

B 32-12 320 12 Fmn 320 - - -

B 35-10 350 10 Fmn 350 MN 35.10 GTS-35 0.8135

P 45-06 450 6 perlitica

Fmp 450 GTS-45 0.8145

P 50-05 500 5 Fmp 500 - - -

P 55-04 550 4 Fmp 550 GTS-55 0.8155

P 60-03 600 3 Fmp 600 - - -

P 65-02 650 2 Fmp 650 GTS-65 0.8165

P 70-02 700 2 Fmp 700 MP 70.2 GTS-70 0.8170

P 80-01 800 1 -

3.4. FONTE CU GRAFIT NODULAR CU STRUCTURA BAINITICA

SR ISO 13169-94 Simbol

STAS

vechi

Marca Rm

N/mm2

A

%

HB

FgnB 800 800 10 260-320 nu exista

FgnB 900 900 8 280-340

FgnB 1000 1000 5 300-380

FgnB 1100 1100 3 360-420

FgnB 1200 1200 2 380-450

FgnB 1400 1400 - 450-550

Document Info

Accesari: 813 Apreciat:

Comenteaza documentul:

Nu esti inregistrat Trebuie sa fii utilizator inregistrat pentru a putea comenta

Creaza cont nou